Q390
作者：上海科涅金属 时间：2023-12-01 浏览：206对应牌号：Q390、Grade55[380]、STKT540、15r2CΦ、HS 390D
Q390A化学成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.035 | ≤0.035 | ≤0.5 | ≤0.1 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 |
Q390B化学成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.035 | ≤0.035 | ≤0.5 | ≤0.1 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 |
Q390C化学成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N | ALs |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.030 | ≤0.030 | ≤0.5 | ≤0.1 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 | ≥0.015 |
Q390D化学成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N | ALs |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.025 | ≤0.030 | ≤0.5 | ≤0.1 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 | ≥0.015 |
Q390E化学成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N | ALs |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.02 | ≤0.025 | ≤0.5 | ≤0.1 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 | ≥0.015 |
力学性能：
【抗拉强度】（σb/MPa）
370-580
【伸长率】（δ5/%）
等级 | δ5/% |
A | ≥19 |
B | ≥19 |
C | ≥20 |
D | ≥20 |
E | ≥20 |
【屈服点】（σs/MPa）
厚度（直径、边长）/mm | ≤16 | >16～35 | >35～50 | >50～100 |
σs/MPa | ≥390 | ≥370 | ≥350 | ≥330 |
【冲击吸收功】（Akv（纵向）/J）
等级￤温度 | +20℃ | 0℃ | -20℃ | -40℃ |
A |
|
|
|
|
B | ≥34 |
|
|
|
C |
| ≥34 |
|
|
D |
|
| ≥34 |
|
E |
|
|
| ≥27 |
特性及应用：
综合力学性能好，焊接性、冷、热加工性能和耐蚀性能均好，C、D、E级钢具有良好的低温韧性。
船舶、锅炉、压力容器、石油储罐、桥梁、电站设备、起重运输机械及其他较高载荷的焊接结构件。